Heavy duty - EP - industrial gear oils of highest performance, outstanding extreme pressure characteristics and load carrying capacityThe RENOLIN CLP 460 products are industrial gear oils of the latest generation, having outstanding extreme pressure characteristics (EP/AW properties) and an extremely high load carrying capacity. They are industrial gear oils with excellent demulsifying properties which can be used in all types of enclosed gear drives with circulation or splash lubrication systems.The RENOLIN CLP 460 products offer extraordinary wear protection. They surpass the requirements in the standard FZG A/8,3/90 scuffing test as well as the more severe FZG test A/16,6/140 double velocity - 16.6 m/s - and increased starting oil sump temperature - 140ºC). The RENOLIN CLP 460 products offer an extremely high micropitting protection (load stage “high” in the load stage test as well as the endurance test). They offer excellent wear protection for roller bearings. The wear rates in the FAG FE8 test are extremely low under these extreme test conditions (7.5 rpm, 80ºC, 80 h, 80 kN).Latest additive technology guarantees excellent wear protection and excellent corrosion protection (steel and copper-containing materials) The RENOLIN CLP  460 products have good elastomer compatibility, stressed static and dynamic elastomers are lubricated and protected from wear. The lifetime of the components is increased. RENOLIN CLP 460 oils can improveequipment reliability and increase productivity.

 The RENOLIN CLP 460 oils are recommended for industrial spur-, helical- and bevel enclosed gears with circulation or splash lubrication, operating at oil temperatures up to 100ºC and peaks above (up to 120ºC).The RENOLIN CLP 460 oils can be used for all applications where lubricants of the CLP type according to DIN 51 517-3 are recommended by the gear manufacturer. These products meet and in many cases exceed the new requirements of well-known gearbox and bearing manufacturers. The RENOLIN CLP 460 oils are particularly suited for gear sets working under heavy load or shock load. They also can be used in non-gear applications including highly loaded, low-speed plain and rolling contact bearings. These mineral oil-based products are designed to provide high quality, latest additive technology of industrial gear oil formulation. They meet the latest industrial standards of well-known OEMs. RENOLIN CLP is approved by company Flender.

 Excellent corrosion protectionLow foaming, excellent air releaseExcellent demulsifying properties (water and watercontaining fluids are rapidly separated)High oxidation resistanceExtremely high load-carrying capacity, extreme pressure-, anti-wear performanceExcellent bearing wear protection (under mixed friction conditions) – FE8Excellent protection from scuffing, excellent wear protection - FZGExcellent micropitting resistance in the load stage and endurance testHigh Brugger wear protectionExcellent elastomer compatibility (static and dynamic)Good compatibility with paint materials

The RENOLIN CLP 460 oils meet and in many cases exceed the requirements:DIN 51 517-3 (2004): CLPISO 6743-6 and ISO 12925-1: CKC / CKDAGMA 9005/E02: EPAIST 224David Brown S1 53.101The products of the RENOLIN CLP 460 are approved for example by:A. Friedrich Flender AG, Bocholt, Germany, Flender BA 7300, table AMüller Weingarten AG, Germany DT 55 005, 10/2003 

  RENOLIN CLP   460   Characteristics Unit   Test Method ISO VG   460 DIN 51 519 Kinematic viscosity      DIN EN ISO 3104 at 40ºC mm2/s 460   at 100ºC mm2/s 30.4   Viscosity index - 95 DIN ISO 2909 Density at 15ºC kg/m3 901 DIN 51 757 Colour ASTM 5.5 DIN ISO 2049 Flash point ºC 270 DIN ISO 2592 Pourpoint ºC -12 DIN ISO 3016 Neutralisation number mgKOH/g 0.6 DIN 51 558-1 Demulsibility at 54ºC min - DIN ISO 6614 Demulsibility at 82ºC min 25 DIN ISO 6614 Copper Corrosion Degree of corrosion   DIN EN ISO 2160 3h, 100ºC (100 A3)   1   Corrrosion protection - steel Degree of corrosion   DIN ISO 7120 Procedure A: dist. water   0   Procedure B: sea water   0   Foaming      ASTM D 892 Seq. I ml 0/0   Seq. II ml 0/0   Seq. III ml 0/0   FZG A/8, 3/90 gear test rig  failure load stage   DIN ISO 14635-1 Start temperature: 90ºC   >14   FZG A/16, 6/140 gear test rig failure load stage   DIN ISO 14635-1 Start temperature: 140ºC   >12   FZG-GFT* test GT-C/8, 3/90 GF Class GFT high FVA-Information Load stage test     Sheet No. 54/I-IV FZG-GFT* test GT-C/8, 3/90 GF Class GFT high FVA-Information Endurance test     Sheet No. 54/I-IV FE8 wear test, D7, 5/80-80     DIN 51 819-3 Roller wear mg <5   Testing in mixed friction area according to Brugger N/mm2   DIN 51 347-2     >50   Timken OK load Lbs 95 ASTM D 2782 4-Ball EP test N >2400 DIN 51 350-2 Weld load Kg >250 ASTM D 2783-88 Elastomer compatibility     Fuchs in house test
 according to DIN ISO 1817 and according to Flender - dynamic and static:       72NBR902 (1000h, 80ºC-dynamic)       75FPM585 (1000h, 90ºC-dynamic)   pass   75FKM17055 (1000h, 90ºC-dynamic)       SRE-NBR 28/SX according to DIN ISO 13226
(100ºC, 7 d static)   pass